- Code
- AS1402 Feature
- Feature 1
- Fast heat cure
- Feature 2
- Good adhesion to most substrates
- Feature 3
- Non slumping paste
- Feature 4
- Translucent
- 100% Modulus (N/mm2)
- 0.54 MPa
- Appearance
- Thixotropic paste
- Color
- Translucent
- Cure Profile
- 1 hour at 150°C, 2 hours at 100°C
- Cure Type
- Addition Heat Cure
- Density
- 1.03 g/cm3
- Dielectric Strength (V/mil)
- 457 V/mil
- Dielectric Strength kV/mm
- 18 kV/mm
- Elongation at Break
- 295 %
- Extrusion Rate g/min
- 440 g/min
- Hardness Shore A
- 30
- Lap Shear Aluminium kg/cm²
- 8.25 kg/cm²
- Linear Coefficient of Thermal Expansion (ppm/°C)
- 291 ppm/°C
- Linear Shrinkage (%)
- 2 %
- Max Storage Temperature
- 15 °C
- Max Working Temp
- 200 °C
- Min Storage Temperature
- -5 °C
- Min Working Temp
- -50 °C
- Rheology
- Paste
- RTV or Heat cure
- Heat cure
- Self Bonding
- Yes
- Shelf Life
- 6 mths
- Tear Resistance (N/mm)
- 3.1 N/mm
- Tensile Strength
- 1.5 N/mm2
- Test Conditions
- After 1 hour at 150°C
- Thermal Conductivity
- 0.2 W/mK
- Volume Coefficient of Thermal Expansion (ppm/°C)
- 874 ppm/°C
- Volume Resistivity (Ohms cm)
- >1E+15 ohms cm
- Youngs Modulus (N/mm2)
- 0.38 N/mm2