- Code
- Silcoset 153 Feature
- Feature 1
- UL recognised in file No. E334038
- Feature 2
- Aerospace approved Rolls Royce MSRR 9410
- Feature 3
- Flexible from -60°C/140°F to +250°C/482°F
- Feature 4
- Excellent adhesion to many substrates
- 100% Modulus (N/mm2)
- 0.91 MPa
- Appearance
- Thixotropic paste
- Color
- Translucent
- CTE Linear ppm/°C
- 292 ppm / °C
- CTE Volumetric ppm/°C
- 876 ppm/°C
- Cure Profile
- 23+/-2°C and 60+/-5% humidity
- Cure Through to 3 mm Depth
- 7 hr
- Cure Type
- Acetoxy
- Density
- 1.05 g/cm3
- Dielectric Constant
- 3.2
- Dissipation Factor
- 0.0012
- Elongation at Break
- 280 %
- Extrusion Rate g/min
- 304 g/min
- Hardness IRHD
- 39
- Linear Shrinkage (%)
- 0.9 %
- Max Storage Temperature
- 40 °C
- Max Working Temp
- 250 °C
- Min Working Temp
- -60 °C
- Rheology
- Paste
- RTV or Heat cure
- RTV
- Self Bonding
- Yes
- Shelf Life
- 24 mths
- Tack Free Time / Skin Formation at 23°C/73°F
- 4 min
- Tear Resistance (N/mm)
- 5.5 N/mm
- Tensile Strength
- 2.32 N/mm2
- Test Conditions
- 7 days at 23+/-2°C and 60+/-5% humidity
- Thermal Conductivity
- 0.2 W/mK
- UL File No.
- E334038
- Volume Resistivity (Ohms cm)
- 4.7E+14 ohms cm
- Youngs Modulus (N/mm2)
- 0.65 N/mm2