- Code
- AS1700 Feature
- Feature 1
- Non corrosive
- Feature 2
- Excellent adhesion to most substrates
- Feature 3
- Excellent dielectric and isolating properties
- Feature 4
- Low odour
- 100% Modulus (N/mm2)
- 0.61 MPa
- Appearance
- Thixotropic paste
- Color
- Translucent
- Cure Profile
- 23+/-2°C and 50+/-5% humidity
- Cure Through to 3 mm Depth
- 36 hr
- Cure Type
- Alkoxy
- Density
- 1.1 g/cm3
- Dielectric Constant
- 3
- Dielectric Strength (V/mil)
- 457 V/mil
- Dielectric Strength kV/mm
- 18 kV/mm
- Dissipation Factor
- 0.0025
- Elongation at Break
- 545 %
- Extrusion Rate g/min
- 290 g/min
- Hardness Shore A
- 30
- Lap Shear Aluminium kg/cm²
- 4.00 kg/cm²
- Lap Shear Copper kg/cm²
- 3.98 kg/cm²
- Lap Shear Polycarbonate Steel kg/cm²
- 5.22 kg/cm²
- Lap Shear Stainless Steel 304 kg/cm²
- 3.04 kg/cm²
- Linear Coefficient of Thermal Expansion (ppm/°C)
- 270 ppm/°C
- Linear Shrinkage (%)
- 1 %
- Max Storage Temperature
- 40 °C
- Max Working Temp
- 200 °C
- Min Working Temp
- -50 °C
- Rheology
- Paste
- RTV or Heat cure
- RTV
- Self Bonding
- Yes
- Shelf Life
- 12 mths
- Slump
- 1 mm/5mins
- Tack Free Time / Skin Formation at 23°C/73°F
- 10 min
- Tear Resistance (N/mm)
- 12.3 N/mm
- Tensile Strength
- 2.43 N/mm2
- Test Conditions
- 7 days at 23+/-2°C and 50+/-5% humidity
- Thermal Conductivity
- 0.2 W/mK
- Volume Coefficient of Thermal Expansion (ppm/°C)
- 810 ppm/°C
- Volume Resistivity (Ohms cm)
- 2.20E+15 ohms cm
- Youngs Modulus (N/mm2)
- 0.54 N/mm2