- Code
- Silcoset 158
- Sub Group
- None Feature
- Feature 1
- High temperature resistance
- Feature 2
- Aerospoace approved
- Feature 3
- Resistant to solvents and chemicals
- Feature 4
- Excellent adhesion to most substrates
- Old Code
- RTV 1008A
- Appearance
- Black paste
- Test Conditions
- After 7 days cure at 23°+/-2°C and 60+/-5% humidity
- Colour
- Black
- SG
- 1.07
- Min Working Temp - °C
- -60 °C
- Max Working Temp +°C
- 300 °C
- FDA
- No
- Shelf life
- 24 mths
- Max storage temperature °C
- 40 °C
- Pack Type
- 1-Part
- Rheology
- Paste
- Non Corrosive
- No
- Cure Type
- Acetoxy
- RTV or Heat cure
- RTV
- Self Bonding
- Yes
- UL 94V-0
- No
- Hardness IRHD
- 38
- Tensile MPa
- 2.3 MPa
- Elongation %
- 290 %
- Tear kN/m
- 5.5 kN/m
- Extrusion Rate g/min
- 270 g/min
- Modulus Youngs MPa
- 0.7 MPa
- Modulus @ 100% Strain MPa
- 0.94 MPa
- Linear Shrinkage %
- 0.8 %
- CTE Volumetric ppm/°C
- 924 ppm/°C
- CTE Linear ppm/°C
- 308 ppm/°C
- Tack Free Time mins
- 4 mins
- Max Cure Hrs @ 25 °C
- 7 hrs
- Thermal Conductivity W/mK
- 0.2 W/mK
- Volume Resistivity ohms cm
- 1E+16 ohms cm
- Surface Resistivity ohms
- 3.57E+15 ohms
- Dielectric Strength kV/mm
- 18 kV/mm
- Dielectric Constant @ 1kHz
- 3
- Dissipation Factor @ 1kHz
- 0.0025
- Lap Shear Aluminium kg/cm²
- 10.01 kg/cm²